1.1 本规范涵盖由未着色聚四氟乙烯制成的未烧结挤出薄膜或胶带，标称厚度为0.025至0.51 mm（0.001至0.020 in.），哪些是 ≥ 99 % 组成中的PTFE。 注1: 对于非烧结着色产品，请参阅规范 D7193 . 1.1.1 目前尚未确定使用回收聚四氟乙烯生产未烧结挤出薄膜或胶带。当商业可用工艺和材料可用时，本规范将进行修订，以包括回收材料。 1.2 以国际单位制表示的数值详见 IEEE/ASTM SI-10 将被视为标准。括号中给出的值仅供参考。 1.3 以下预防说明仅适用于试验方法部分第节 8. 本规范: 本标准并非旨在解决与其使用相关的所有安全问题（如有）。本标准的用户有责任在使用前制定适当的安全、健康和环境实践，并确定监管限制的适用性。 注2: 尽管本规范和ISO 13000-1和ISO 13000-2在方法或细节上有所不同，使用这两种方法获得的与特定特性相关的数据在技术上是等效的。 1.4 本国际标准是根据世界贸易组织技术性贸易壁垒（TBT）委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认标准化原则制定的。

1.1 This specification covers unsintered extruded films or tapes manufactured from virgin, unpigmented polytetrafluoroethylene, in nominal thickness from 0.025 to 0.51 mm (0.001 to 0.020 in.), which are ≥ 99 % PTFE in composition. Note 1: For unsintered pigmented products, refer to Specification D7193 . 1.1.1 The use of recycled PTFE for production of unsintered extruded films or tapes has not been identified at this time. When commercial usable processes and materials are available, this specification will be revised to include recycled materials. 1.2 The values stated in SI units are detailed in IEEE/ASTM SI-10 are to be regarded as the standard. The values given in parentheses are for information only. 1.3 The following precautionary statement pertains only to the test method portion, Section 8 of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Note 2: Although this specification and ISO 13000-1 and ISO 13000-2 differ in approach or detail, data obtained relating to specific properties, using either are technically equivalent. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.