1.1 本试验方法包括使用断层测功机测量安装在试样支架上并在规定载荷下承受切削刃的材料的切削阻力。 2. 1.1.1 该程序不适用于允许切削刃在切削前与安装表面接触的高孔隙率材料。 1.1.2 测试设备在测试厚度大于20mm的材料时可能有局限性。 1.2 以国际单位制表示的数值应视为标准。国际单位制后括号中给出的值仅供参考，不被视为标准值。 1.3 本标准并非旨在解决与其使用相关的所有安全问题（如有）。本标准的使用者有责任在使用前制定适当的安全、健康和环境实践，并确定监管限制的适用性。 1.4 本国际标准是根据世界贸易组织技术性贸易壁垒委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认的标准化原则制定的。 ====意义和用途====== 5.1 该试验方法评估材料在规定载荷下暴露于切削刃时的抗切割性。从该测试方法获得的数据可用于比较不同材料的耐切割性。 5.2 该测试方法仅针对与材料表面光滑锋利边缘的切割动作相关的切割危险范围。它不代表材料可能受到的任何其他切割危险，如锯齿状边缘、锯片或电动切割工具。它也不能代表刺破、撕裂或其他织物失效模式。

1.1 This test method covers the measurement of the cut resistance of a material when mounted on a specimen holder and subjected to a cutting edge under a specified load using a tomodynamometer. 2 1.1.1 This procedure is not valid for high-porosity materials which allow cutting edge contact with the mounting surface prior to cutting. 1.1.2 Test apparatus may have limitations in testing materials with a thickness greater than 20 mm. 1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. ====== Significance And Use ====== 5.1 This test method assesses the cut resistance of a material when exposed to a cutting edge under specified loads. Data obtained from this test method can be used to compare the cut resistance of different materials. 5.2 This test method only addresses that range of cutting hazards that are related to a cutting action by a smooth sharp edge across the surface of the material. It is not representative of any other cutting hazard to which the material may be subjected, such as serrated edges, saw blades, or motorized cutting tools. Nor is it representative of puncture, tear, or other modes of fabric failure.