AWS B2.1-5A-223:1999(R2009)-铬钼钢（M-5A/P-5A）的保护金属极电弧焊标准焊接工艺规范（SWPS） E9018-B3 1/8至1/2英寸厚如焊接状态；1/8至1-1/2英寸厚焊后热处理条件主要用于管道应用-国家数字标准馆

现行 AWS B2.1-5A-223:1999(R2009)

到馆提醒

收藏跟踪

购买正版

Standard Welding Procedure Specification (SWPS) for Shielded Metal Arc Welding of Chromium-Molybdenum Steel (M-5A/P-5A), E9018-B3, 1/8 through 1/2 in. Thick, As-Welded Condition; 1/8 through 1-1/2 in. Thick, PWHT Condition, Primarily Pipe Applications 铬钼钢（M-5A/P-5A）的保护金属极电弧焊标准焊接工艺规范（SWPS） E9018-B3 1/8至1/2英寸厚如焊接状态；1/8至1-1/2英寸厚焊后热处理条件主要用于管道应用

发布日期： 1999-12-08

本标准包含厚度为1/8的铬钼钢的基本焊接变量
通过1/2英寸。在焊接状态下；或者1/8到1-1/2英寸。在焊后热处理（PWHT）条件下，使用
手工保护金属电弧焊。它引用了制造焊接件所需的基本金属和操作条件
填充金属规范，以及坡口焊缝的允许接头设计。本标准焊接工艺规范
（SWPS）主要用于管道应用。

This standard contains the essential welding variables for chromium-molybdenum steel in the thickness range of 1/8
through 1/2 in. in the as-welded condition; or 1/8 through 1-1/2 in. in the postweld heat treated (PWHT) condition, using
manual shielded metal arc welding. It cites the base metals and operating conditions necessary to make the weldment, the
filler metal specifications, and the allowable joint designs for groove welds. This standard welding procedure specification
(SWPS) was developed primarily for pipe applications.

分类信息

发布单位或类别：美国-美国焊接协会

关联关系

研制信息

相似标准/计划/法规

1A1W1S1 Archive Product 133

Standard Welding Procedure Specification (Swps) for Shielded Metal Arc Welding of Galvanized Steel (M-1), 10 through 18 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下10至18号镀锌钢（M-1）带或不带衬垫的保护金属极电弧焊标准焊接工艺规范（Swps）

AWS B2.1.011-91

Standard Welding Procedure Specification for Shielded Metal Arc Welding of Galvanized Steel, 10 through 18 Gauge, in the As-Welded Condition, With of Without Backing
无背衬焊态10至18号镀锌钢的保护金属极电弧焊标准焊接工艺规范

AWS B2.1-1-012-2002(R2013)

Standard Welding Procedure Specification (Swps) for Shielded Metal Arc Welding of Carbon Steel (M-1, P-1, or S-1 to M-1, P-1, or S-1), 10 through 18 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下10至18 Gauge碳钢（M-1、P-1或S-1至M-1、P-1或S-1）带或不带衬垫的保护金属极电弧焊标准焊接工艺规范（Swps）

1A1W1S1 Archive Product 127

Standard Welding Procedure Specification (Swps) for Gas Metal Arc Welding (Short Circuiting Transfer Mode) of Galvanized Steel (M-1), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号镀锌钢（M-1）气体保护金属极电弧焊（短路过渡模式）的标准焊接工艺规范（Swps）带或不带衬垫

AWS B2.1-1/8-014-2002(R2013)

Standard Welding Procedure Specification (Swps) for Shielded Metal Arc Welding of Carbon Steel to Austenitic Stainless Steel (M-1 to M-8/P-8/S-8, Group 1), 10 through 18 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下带或不带衬垫的10至18 Gauge碳钢至奥氏体不锈钢（M-1至M-8/P-8/S-8 第1组）的保护金属极电弧焊标准焊接工艺规范（Swps）

AWS B2.1-1-007-2002(R2013)

Standard Welding Procedure Specification (Swps) for Gas Tungsten Arc Welding of Galvanized Steel (M-1), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号镀锌钢（M-1）带或不带衬垫的钨极气体保护焊标准焊接工艺规范（Swps）

AWS B2.1-1-004-2002(R2013)

Standard Welding Procedure Specification (Swps) for Gas Metal Arc Welding (Short Circuiting Transfer Mode) of Carbon Steel (M-1, Group 1), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号规格碳钢（M-1 第1组）带或不带衬垫的气体保护金属极电弧焊（短路过渡模式）的标准焊接工艺规范（Swps）

AWS B2.1.012-91

Standard Welding Procedure Specification for Shielded Metal Arc Welding of Carbon Steel, (M-1, Group 1), 10 through 18 Gauge, in the As-Welded Condition, With or Without Backing
焊接状态下带或不带衬垫的10至18号规格碳钢（M-1 第1组）的保护金属极电弧焊的标准焊接工艺规范

AWS B2.1.013-91

Standard Welding Procedure Specification for Shielded Metal Arc Welding of Austenitic Stainless Steel, (M-8 or P-8), 10 through 18 Gauge, in the As-Welded Condition, With or Without Backing
焊接状态下10至18号奥氏体不锈钢（M-8或P-8）带或不带衬垫的保护金属极电弧焊的标准焊接工艺规范

AWS B2.1-1-233-2006

Standard Welding Procedure Specification (Swps) for Argon Plus 25% Carbon Dioxide Shielded Gas Metal Arc Welding (Short Circuting Transfer Mode) followed by Argon Plus 2% Oxygen Shielded Gas Metal Arc Welding (Spray Transfer Mode) of Carbon Steel (M-1/P-1/S-1) Groups 1 and 2, 1/8 through 1-1/2 inch
碳钢（M-1/P-1/S-1）组1和2、1/8至1-1/2英寸的氩加25%二氧化碳气体保护金属极弧焊（短路过渡模式）和氩加2%氧气保护气体保护金属极弧焊（喷射过渡模式）的标准焊接工艺规范（Swps）

AWS B2.1-5A-224-1999(R2009)

Standard Welding Procedure Specification (SWPS) for Gas Tungsten Arc Welding followed by Shielded Metal Arc Welding of Chromium-Molybdenum Steel (M-5A/P-5A), 1/8 through 1/2 in. Thick, As-Welded Condition; 1/8 through 1-1/2 in. Thick, PWHT Condition, ER90S-B3 and E9018-B3, Primarily Pipe Applic
1/8至1/2英寸铬钼钢（M-5A/P-5A）的气体保护钨极电弧焊后的标准焊接工艺规范（SWPS）厚如焊接状态；1/8至1-1/2英寸厚度焊后热处理条件 ER90S-B3和E9018-B3 主要用于管道应用

AWS B2.1-5A-226-1999(R2009)

Standard Welding Procedure Specification (SWPS) for Gas Tungsten Arc Welding (Consumable Insert Root) followed by Shielded Metal Arc Welding of Chromium-Molybdenum Steel (M-5A/P-5A), 1/8 through 1/2 in. Thick, As-Welded Condition; 1/8 through 1-1/2 in. Thick, PWHT Condition, IN521, ER90S-B3, and E9
1/8至1/2英寸铬钼钢（M-5A/P-5A）的气体保护钨极电弧焊（自耗镶块根部）和金属保护电弧焊的标准焊接工艺规范（SWPS）厚如焊接状态；1/8至1-1/2英寸厚度、焊后热处理条件、IN521、ER90S-B3和E9

AWS B2.1-8-023-2018

Standard Welding Procedure Specification (SWPS) for Shielded Metal Arc Welding of Austenitic Stainless Steel (M-8/P-8, Group 1), 1/8 inch [3 mm] through 1-1/2 inch [38 mm] Thick, As-Welded Condition, Primarily Plate and Structural Applications
1/8英寸[3 mm]至1-1/2英寸[38 mm]厚的焊态奥氏体不锈钢（M-8/P-8 第1组）的保护金属电弧焊标准焊接工艺规范（SWPS）主要用于板材和结构应用

AWS B2.1-1/8-229-2002-AMD1(R2013)

STANDARD WELDING PROCEDURE SPECIFICATION (SWPS) FOR GAS TUNGSTEN ARC WELDING FOLLOWED BY SHIELDED METAL ARC WELDING OF CARBON STEEL (M-1/P-1/S-1, GROUPS 1 OR 2) TO AUSTENITIC STAINLESS STEEL (M-8/P-8/S-8, GROUP 1), 1/8 THROUGH 1-1/2 INCH
碳钢（M-1/P-1/S-1 第1组或第2组）与奥氏体不锈钢（M-8/P-8/S-8 第1组） 1/8至1-1/2英寸的气体保护金属极电弧焊后的钨极气体保护焊标准焊接工艺规范（SWPS）

AWS B2.1-8-005-2002(R2013)

Standard Welding Procedure Specification (Swps) for Gas Metal Arc Welding (Short Circuiting Transfer Mode) of Austenitic Stainless Steel (M-8, P-8, or S-8), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
18至10号奥氏体不锈钢（M-8、P-8或S-8）焊态气体保护焊（短路过渡模式）标准焊接工艺规范（Swps）带或不带衬垫

1A1W1S1 Archive Product 344

Standard Welding Procedure Specification (Swps) for Gas Tungsten Arc Welding of Aluminum (M/P/S-22 to M/P/S-22), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号铝（M/P/S-22至M/P/S-22）带或不带衬垫的钨极气体保护焊标准焊接工艺规范（Swps）

AWS B2.1-8-009-2002(R2013)

Standard Welding Procedure Specification (Swps) for Gas Tungsten Arc Welding of Austenitic Stainless Steel (M-8, P-8, or S-8), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号奥氏体不锈钢（M-8、P-8或S-8）带或不带衬垫的钨极气体保护焊标准焊接工艺规范（Swps）

1A1W1S1 Archive Product 464

Standard Welding Procedure Specification for Naval Applications (SWPS-N) for Shielded Metal Arc Welding of Carbon Steel (S-1), 1/8 inch [3 mm] through 1-1/2 inch [38 mm] Thick, MIL-7018-M, in the As-Welded or PWHT Condition, Primarily Pipe for Naval Applications
MIL-7018-M 厚度为1/8英寸[3 mm]至1-1/2英寸[38 mm]的碳钢（S-1）在焊态或焊后热处理条件下主要用于海军应用的管道的保护金属极电弧焊的海军应用标准焊接工艺规范（SWPS-N）

AWS B2.1-1-232-2006

Standard Welding Procedure Specification (Swps) for Argon Plus 25% Carbon Dioxide Shielded Gas Metal Arc Welding (Short Circuting Transfer Mode) followed by Argon Plus 25% Carbon Dioxide Shielded Flux Cored Arc Welding of Carbon Steel (M-1/P-1/S-1, Groups 1 and 2), 1/8 through 1-1/2 inch Thick, ER70
1/8至1-1/2英寸厚ER70碳钢（M-1/P-1/S-1 第1组和第2组）氩加25%二氧化碳保护气体保护金属弧焊（短路过渡模式）和氩加25%二氧化碳保护药芯焊丝电弧焊的标准焊接工艺规范（Swps）

AWS B2.1.001-90

Standard Welding Procedure Specification for Shielded Metal Arc Welding of Carbon Steel, (M-1/P-1, Group 1 or 2), 3/16 through 3/4 inch, in the as-Welded Condition, With Backing
3/16至3/4英寸碳钢（M-1/P-1 第1组或第2组）在焊接状态下带衬垫的保护金属极电弧焊的标准焊接工艺规范

《国家标准化发展纲要》提出建设国家数字标准馆，推动标准化工作向数字化、网络化、智能化转型。中国标准化研究院正在全力推进国家数字标准馆建设，力争在2026年底建成“一个中心”和“一个平台”，即全球领先的标准数据资源中心，涵盖标准全生命周期的数字化、网络化、智能化研究与服务平台。

专题数据库

标准管理系统

大数据分析系统

标准智能研制系统