1.1 这些试验方法包括硅酸盐水泥混凝土和沥青混凝土路面用热涂型接缝和裂缝密封剂及填料的试验。有许多标准材料规范使用这些测试方法。参考相关标准材料规范，以确定使用以下哪种测试方法。关于样品熔化和混凝土砌块制备，请参见各自的标准做法。 1.2 试验方法见以下章节: 部分 人工风化 13 沥青相容性 12 粘结，非浸没 8. 粘合剂，浸水 9 锥体贯入度，非- 浸没 6. 灵活性 15 流 7. 恢复力 10 弹性，烘箱老化 11 拉伸附着力 14 1.3 以国际单位制表示的数值应视为标准值。本标准不包括其他计量单位。 1.4 本标准并非旨在解决与其使用相关的所有安全问题（如有）。本标准的用户有责任在使用前制定适当的安全、健康和环境实践，并确定监管限制的适用性。 1.5 本国际标准是根据世界贸易组织技术性贸易壁垒（TBT）委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认标准化原则制定的。 ====意义和用途====== 3.1 这些试验方法描述了确定热应用、现场模制接缝和裂缝密封剂及填料规范符合性的程序。

1.1 These test methods cover tests for hot-applied types of joint and crack sealants and fillers for portland cement concrete and asphaltic concrete pavements. There are numerous standard material specifications that use these test methods. Refer to the respective standard material specification of interest to determine which of the following test methods to use. For sample melting and concrete block preparation, see their respective standard practices. 1.2 The test methods appear in the following sections: Section Artificial Weathering 13 Asphalt Compatibility 12 Bond, Non-Immersed 8 Bond, Water-Immersed 9 Cone Penetration, Non-Immersed 6 Flexibility 15 Flow 7 Resilience 10 Resilience, Oven-Aged 11 Tensile Adhesion 14 1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. ====== Significance And Use ====== 3.1 These test methods describe procedures for determining specification conformance for hot-applied, field-molded joint and crack sealants and fillers.