SAE AMS3970/1A-120°C（250°F）真空固化碳纤维织物修补预浸料第1部分-一般要求-国家数字标准馆

现行 SAE AMS3970/1A

到馆提醒

收藏跟踪

购买正版

Carbon Fiber Fabric Repair Prepreg, 120 °C (250 °F) Vacuum Curing Part 1 - General Requirements 120°C（250°F）真空固化碳纤维织物修补预浸料第1部分-一般要求

发布日期： 2016-12-06

AMS 3970/1给出了用于修复碳纤维增强环氧结构的碳纤维织物环氧预浸料和配套非结构玻璃预浸料的技术要求和鉴定程序。预浸料系统可包括在与预浸料的共固化过程中应用的薄膜粘合剂，用于接合和夹层粘合。筛选试验期间，应确定是否需要薄膜粘合剂。

AMS 3970/1 gives information about the technical requirements and qualification procedure for carbon fiber fabric epoxy prepreg and a companion non-structural glass prepreg used for repair of carbon fiber reinforced epoxy structures. The prepreg system may include a film adhesive to be applied in a co-curing process with the prepreg for joint and sandwich bonding. The need for a film adhesive shall be established during screening tests.

分类信息

发布单位或类别：美国-美国机动车工程师协会

关联关系

研制信息

相似标准/计划/法规

Carbon Fiber Fabric Repair Prepreg, 120 °C (250 °F) Vacuum Curing Part 0 - Introduction
120°C（250°F）真空固化碳纤维织物修补预浸料第0部分-简介

Carbon Fiber Fabric Repair Prepreg, 120 °C (250 °F) Vacuum Curing Part 3 - Purchasing Specification for Carbon Prepreg
120°C（250°F）真空固化碳纤维织物修补预浸料第3部分-碳预浸料采购规范

Carbon Fiber Fabric Repair Prepreg, 120 °C (250 °F) Vacuum Curing Part 4 - Purchasing Specification for Film Adhesive
120°C（250°F）真空固化碳纤维织物修补预浸料第4部分-薄膜粘合剂采购规范

Carbon Fiber Fabric Repair Prepreg, 120 °C (250 °F) Vacuum Curing Part 5 - Purchasing Specification for Companion Non-Structural Glass Fiber Fabric Prepreg
120°C（250°F）真空固化碳纤维织物修补预浸料第5部分-配套非结构玻璃纤维织物预浸料采购规范

Carbon Fiber Fabric Repair Prepreg, 120 °C (250 °F) Vacuum Curing Part 2 - Qualification Program for Fiber, Fabric, Carbon Prepreg, Film Adhesive and Non-Structural Glass Prepreg
120°C（250°F）真空固化碳纤维织物修补预浸料第2部分-纤维、织物、碳预浸料、薄膜粘合剂和非结构玻璃预浸料的鉴定程序

Unidirectional Carbon Fiber Tape Epoxy Repair Prepreg, Vacuum Curing Part 5 - Material Specification for Unidirectional Carbon Fiber Tape Epoxy Prepreg for Repair and Film Adhesive for Repair, 120 to 145 °C (250 to 290 °F) Curing
真空固化单向碳纤维带环氧树脂修补预浸料第5部分-120至145℃（250至290℉）固化的修补用单向碳纤维带环氧树脂预浸料和修补用薄膜粘合剂的材料规范

Carbon Fiber Fabric Repair Prepreg, 120 °C (250 °F) Vacuum Curing Part 6 - Material Specification: Carbon Fiber Fabric Reinforced Epoxy Prepreg for Repair, Plain Weave Fabric, 193 g/m2, Adhesive Film for Repair and Non-Structural Glass Fiber Fabric Reinforced Epoxy Prepreg, 105 g/m2
120°C（250°F）真空固化碳纤维织物修补预浸料第6部分-材料规范:修补用碳纤维织物增强环氧预浸料平纹织物193g/m2修补用粘合膜和非结构玻璃纤维织物增强环氧预浸料105g/m2

《国家标准化发展纲要》提出建设国家数字标准馆，推动标准化工作向数字化、网络化、智能化转型。中国标准化研究院正在全力推进国家数字标准馆建设，力争在2026年底建成“一个中心”和“一个平台”，即全球领先的标准数据资源中心，涵盖标准全生命周期的数字化、网络化、智能化研究与服务平台。

专题数据库

标准管理系统

大数据分析系统

标准智能研制系统