1.1 本试验方法包括根据抗弹性曲率半径确定夹层蜂窝芯的泊松比；看见 图1 . 图1 反弹性曲率 1.2 单位- 以国际单位制或英寸-磅单位表示的数值应单独视为标准值。每个系统中规定的值不一定是精确的等价物；因此，为确保符合本标准，每个系统应独立使用，且两个系统的值不得组合。 1.2.1 在文本中，英寸- 磅单位显示在括号中。 1.3 本标准并非旨在解决与其使用相关的所有安全问题（如有）。本标准的用户有责任在使用前制定适当的安全、健康和环境实践，并确定监管限制的适用性。 1.4 本国际标准是根据世界贸易组织技术性贸易壁垒（TBT）委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认标准化原则制定的。 ====意义和用途====== 5.1 某些夹层板分析需要蜂窝芯的泊松比。传统方法无法测量蜂窝的泊松比。 5.2 本试验方法为蜂窝芯材料的设计性能、材料规范、研发应用和质量保证提供了一种确定泊松比的标准方法。 5.3 影响蜂窝芯材料泊松比的因素，因此应报告如下: 芯材料，材料制造方法，芯几何形状，芯厚度，芯厚度均匀性，细胞壁厚，试样几何形状，试样制备和试样调节。

1.1 This test method covers the determination of the sandwich honeycomb core Poisson's ratio from the anticlastic curvature radii; see Fig. 1 . FIG. 1 Anticlastic Curvature 1.2 Units— The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined. 1.2.1 Within the text, the inch-pound units are shown in brackets. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. ====== Significance And Use ====== 5.1 Certain sandwich panel analyses require the Poisson's ratio of the honeycomb core. It is not possible to measure the honeycomb's Poisson's ratio by conventional methods. 5.2 This test method provides a standard method of determining the Poisson’s ratio of honeycomb core materials for design properties, material specifications, research and development applications, and quality assurance. 5.3 Factors that influence the Poisson’s ratio of honeycomb core materials and shall therefore be reported include the following: core material, methods of material fabrication, core geometry, core thickness, core thickness uniformity, cell wall thickness, specimen geometry, specimen preparation, and specimen conditioning.