Aluminum Alloy, Investment Castings 7.0Si - 0.32Mg (356.0-T6) Solution and Precipitation Heat Treated 铝合金熔模铸件7.0Si-0.32Mg（356.0-T6）固溶和沉淀热处理

发布日期： 2014-10-01

本规范涵盖熔模铸件形式的铝合金。这些铸件通常用于要求低重量、中等强度和坚固性的部件，铸造至接近最终尺寸，但使用不限于此类应用。

This specification covers an aluminum alloy in the form of investment castings.These castings have been used typically for components requiring low weight, moderate strength and soundness, cast to approximately final dimensions, but usage is not limited to such applications.

分类信息

发布单位或类别：美国-美国机动车工程师协会

关联关系

研制信息

相似标准/计划/法规

Aluminum Alloy, Castings 7.0Si - 0.32Mg (356.0-T6) Solution and Precipitation Heat Treated
铝合金铸件7.0Si-0.32Mg（356.0-T6）固溶和沉淀热处理

Aluminum Alloy Castings, Investment 7.0Si - 0.32Mg (356.0-T51) Precipitation Heat Treated
铝合金铸件熔模7.0Si-0.32Mg（356.0-T51）沉淀热处理

Aluminum Alloy Castings, Centrifugal 7.0Si - 0.30Mg (356.0-T6) Solution and Precipitation Heat Treated
经固溶和沉淀热处理的离心式7.0Si-0.30Mg（356.0-T6）铝合金铸件

Aluminum Alloy Castings, Permanent Mold 7.0Si - 0.32Mg (356.0-T51) As-Cast then Precipitation Heat Treated
铝合金铸件永久模7.0Si-0.32Mg（356.0-T51）铸态然后进行沉淀热处理

Aluminum Alloy Castings, Permanent Mold 7.0Si - 0.30Mg (356.0-T6) Solution and Precipitation Heat Treated
铝合金铸件永久模7.0Si-0.30Mg（356.0-T6）固溶和沉淀热处理

Aluminum Alloy Castings 7.0Si - 0.55Mg - 0.12Ti (F357.0-T6) Solution and Precipitation Heat Treated
铝合金铸件7.0Si-0.55Mg-0.12Ti（F357.0-T6）固溶和沉淀热处理

Aluminum Alloy Castings 7.0Si - 0.58Mg - 0.15Ti (E357.0-T6) Solution and Precipitation Heat Treated
铝合金铸件7.0Si-0.58Mg-0.15Ti（E357.0-T6）固溶和沉淀热处理

Aluminum Alloy Castings 7.0Si - 0.55Mg - 0.12Ti - 0.06Be (A357.0 T6) Solution and Precipitation Heat Treated
铝合金铸件7.0Si-0.55Mg-0.12Ti-0.06Be（A357.0 T6）固溶和沉淀热处理

Aluminum Alloy Castings 7.0Si - 0.35Mg (A356.0-T6) (Formerly T6P Temper) Solution and Precipitation Heat Treated
铝合金铸件7.0Si-0.35Mg（A356.0-T6）（原T6P回火）固溶和沉淀热处理

Aluminum Alloy Castings 7.0Si - 0.58Mg - 0.15Ti - 0.06Be (D357.0-T6) Solution and Precipitation Heat Treated (Requiring Fatigue and Fracture Toughness Testing)
铝合金铸件7.0Si-0.58Mg-0.15Ti-0.06Be（D357.0-T6）固溶和沉淀热处理（需要进行疲劳和断裂韧性测试）

Aluminum Alloy Castings 7.0Si - 0.58Mg - 0.15Ti - 0.06Be (D357.0-T6) Solution and Precipitation Heat Treated Dendrite Arm Spacing (DAS) Controlled
铝合金铸件7.0Si-0.58Mg-0.15Ti-0.06Be（D357.0-T6）固溶和沉淀热处理枝晶臂间距（DAS）受控

《国家标准化发展纲要》提出建设国家数字标准馆，推动标准化工作向数字化、网络化、智能化转型。中国标准化研究院正在全力推进国家数字标准馆建设，力争在2026年底建成“一个中心”和“一个平台”，即全球领先的标准数据资源中心，涵盖标准全生命周期的数字化、网络化、智能化研究与服务平台。

专题数据库

标准管理系统

大数据分析系统

标准智能研制系统