AWS B2.1-1-207:2019-标准焊接工艺规范（WPS）；碳钢的钨极气体保护焊（M-1/P-1/S-1 第1组或第2组） 1/8至1-1/2英寸 ER70S-2 焊前或焊后热处理条件（主要是管道应用）-国家数字标准馆

现行 AWS B2.1-1-207:2019

到馆阅读

收藏跟踪

购买正版

Standard Welding Procedure Sspecification (WPS) for; Gas Tungsten Arc Welding of Carbon Steel (M-1/P-1/S-1, group 1 or 2), 1/8 through 1-1/2" think, ER70S-2, as-Welded or PWHT Ccondition (primarily pipe applications) 标准焊接工艺规范（WPS）；碳钢的钨极气体保护焊（M-1/P-1/S-1 第1组或第2组） 1/8至1-1/2英寸 ER70S-2 焊前或焊后热处理条件（主要是管道应用）

发布日期： 2019-03-01

AWS B2。1-1-207:2019包含厚度范围为1/8英寸[3 mm]到1-1/2英寸[38 mm]的碳钢的基本焊接变量，使用手动钨极气体保护焊。它引用了制作焊件所需的母材和操作条件、填充金属规范以及角焊缝和坡口焊缝的允许接头设计。该SWPS主要用于管道应用。

AWS B2.1-1-207:2019 contains the essential welding variables for carbon steel in the thickness range of 1/8 inch [3 mm] through 1-1/2 inch [38 mm], using manual gas tungsten arc welding. It cites the base metals and operating conditions necessary to make the weldment, the filler metal specifications, and the allowable joint designs for fillet and groove welds. This SWPS was developed primarily for pipe applications.

分类信息

发布单位或类别：美国-美国焊接协会

关联关系

研制信息

相似标准/计划/法规

1A1W1S1 Archive Product 407

STANDARD WELDING PROCEDURE SPECIFICATION (WPS) FOR GAS TUNGSTEN ARC WELDING OF CARBON STEEL, (M-1/P-1, GROUP 1 OR 2), 3/16 THROUGH 7/8 INCH, IN THE AS-WELDED CONDITION, WITH OR WITHOUT BACKING
3/16至7/8英寸碳钢（M-1/P-1 第1组或第2组）焊态钨极气体保护焊标准焊接工艺规范（WPS）带或不带衬垫

AWS B2.1-1/8-227-2002-AMD1(R2013)

STANDARD WELDING PROCEDURE SPECIFICATION(WPS) FOR; GAS TUNGSTEN ARC WELDISTANDARD WELDING PROCEDURE SPECIFICATION (SWPS) FOR GAS TUNGSTEN ARC WELDING OF CARBON STEEL (M-1/P-1/S-1, GROUPS 1 OR 2) TO AUSTENITIC STAINLESS STEEL (M-8/P-8/S-8, GROUP 1), 1/16 THROUGH 1-1/2 INCH THICK, ER309(L), AS-WELDED
标准焊接工艺规范（WPS）；钨极气体保护焊1/16至1-1/2英寸厚ER309（L）焊态奥氏体不锈钢（M-8/P-8/S-8 1组）与碳钢（M-1/P-1/S-1 1或2组）的钨极气体保护焊标准焊接工艺规范（SWPS）

AWS B2.1-1-007-2002(R2013)

Standard Welding Procedure Specification (Swps) for Gas Tungsten Arc Welding of Galvanized Steel (M-1), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号镀锌钢（M-1）带或不带衬垫的钨极气体保护焊标准焊接工艺规范（Swps）

AWS B2.1.015-91

Standard Welding Procedure Specification for Gas Tungsten Arc Welding of Aluminum, (M-22 or P-22), 10 through 18 Gauge, in the As-Welded Condition, With or Without Backing
焊接状态下带或不带衬垫的10至18号铝（M-22或P-22）气体保护钨极电弧焊的标准焊接工艺规范

AWS B2.1-8-212-2001(R2012)

Standard Welding Procedure Specification (WPS) for Gas Tungsten Arc Welding of Austenitic Stainless Steel (M-8/P-8/S-8, Group 1), 1/8 through 1-1/2 in. Thick, ER3XX, As-Welded Condition, Primarily Pipe Applications
1/8至1-1/2英寸奥氏体不锈钢（M-8/P-8/S-8 第1组）的钨极气体保护焊标准焊接工艺规范（WPS）厚 ER3XX 焊接状态主要用于管道应用

AWS B2.1-8-214-2001(R2012)

Standard Welding Procedure Spec (WPS) for Gas Tungsten Arc Welding Followed by Shielded Metal Arc Welding of Austenitic Stainless Steel (M-8/P-8/S-8, Group 1), 1/8 through 1-1/2 in. Thick, ER3XX, ER3XX-XX, As-Welded Condition, Primarily Pipe Applications
1/8至1-1/2英寸奥氏体不锈钢（M-8/P-8/S-8 第1组）的气体保护钨极电弧焊后的标准焊接工艺规范（WPS）厚 ER3XX ER3XX-XX 焊接状态主要用于管道应用

1A1W1S1 Archive Product 180

Standard Welding Procedure Specification (WPS) for Gas Tungsten Arc Welding followed by Shielded Metal Arc Welding of Chromium-Molybdenum Steel (M-4/P-4, Group 1 or 2), 1/8 through 1/2 in. Thick, As-Welded Condition, As-Welded Condition, 1/8 through 1-1/2 in. Thick, PWHT Condition, ER80S-B2 and E801
1/8至1/2英寸铬钼钢（M-4/P-4 第1组或第2组）的气体保护钨极电弧焊后的标准焊接工艺规范（WPS）厚度焊接状态焊接状态 1/8至1-1/2英寸厚度焊后热处理条件 ER80S-B2和E801

1A1W1S1 Archive Product 344

Standard Welding Procedure Specification (Swps) for Gas Tungsten Arc Welding of Aluminum (M/P/S-22 to M/P/S-22), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号铝（M/P/S-22至M/P/S-22）带或不带衬垫的钨极气体保护焊标准焊接工艺规范（Swps）

AWS B2.1-8-009-2002(R2013)

Standard Welding Procedure Specification (Swps) for Gas Tungsten Arc Welding of Austenitic Stainless Steel (M-8, P-8, or S-8), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号奥氏体不锈钢（M-8、P-8或S-8）带或不带衬垫的钨极气体保护焊标准焊接工艺规范（Swps）

1A1W1S1 Archive Product 37

Standard Welding Procedure Specification for Gas Tungsten Arc Welding Followed by Shielded Metal Arc Welding of Austenitic Stainless Steel (M-8/P-8/S-8, Group 1), 1/8 through 1-1/2 inch Thick, As-Welded Condition
焊接状态下1/8至1-1/2英寸厚的奥氏体不锈钢（M-8/P-8/S-8 第1组）的气体保护钨极电弧焊后的标准焊接工艺规范

1A1W1S1 Archive Product 26

Standard Welding Procedure Specification for Gas Tungsten Arc Welding of Carbon Steel, (M-1/P-1, Group 1 or 2), 3/16 through 7/8 inch, in the As-Welded Condition, With or Without Backing
3/16至7/8英寸碳钢（M-1/P-1 第1组或第2组）在焊接状态下带或不带衬垫的钨极气体保护焊的标准焊接工艺规范

AWS B2.1.010-90

Standard Welding Procedure Specification for Gas Tungsten Arc Welding of Carbon Steel to Austenic Stainless Steel, (M-1 to M-8 or P-8), 10 through 18 Gauge, in the As-Welded Condition, With or Without Backing
在焊态条件下带或不带衬垫的10至18 Gauge碳钢至奥氏体不锈钢（M-1至M-8或P-8）的钨极气体保护焊标准焊接工艺规范

AWS B2.1-4-217-1999(R2009)

Standard Welding Procedure Specification (WPS) for Gas Tungsten Arc Welding of Chromium- Molybdenum Steel (M-4/P-4, Group 1 or 2), ER80S-B2, 1/8 through 1/2 in. Thick, As-Welded Condition, 1/8 through 3/4 in. Thick, PWHT Condition, Primarily Pipe Applications
ER80S-B2 1/8至1/2英寸铬钼钢（M-4/P-4 1或2组）的钨极气体保护焊标准焊接工艺规范（WPS）厚度焊接状态 1/8至3/4英寸厚焊后热处理条件主要用于管道应用

1A1W1S1 Archive Product 36

Standard Welding Procedure Specification for Gas Tungsten Arc Welding of Austenitic Stainless Steel (M-8/P-8/S-8, Group 1), 1/8 through 1-1/2 inch Thick, As-Welded Condition
1/8至1-1/2英寸厚的焊态奥氏体不锈钢（M-8/P-8/S-8 第1组）的钨极气体保护焊标准焊接工艺规范

AWS B2.1-1-211-2001(R2012)

Standard WPS for Gas Tungsten Arc Welding with Consumable Inserts Followed by Shielded Metal Arc Welding of Carbon Steel (M-1/P-1/S-1, Group 1 or 2), 1/8 through 1 1/2" Thick, INMs-1, ER70S-2, and E7018, As-Welded or PWHT Condition, Primarily Pipe App.
1/8至1/2“厚、INMs-1、ER70S-2和E7018的碳钢（M-1/P-1/S-1 第1组或第2组）在焊态或焊后热处理状态下用自耗嵌件进行钨极气体保护焊的标准WPS 主要用于管道应用

AWS B2.1-1/8-010-2015

Standard Welding Procedure Specification (SWPS) for Gas Tungsten Arc Welding of Carbon Steel (M-1/P-1), to Austenitic Stainless Steel (M-8/P-8), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
焊接状态下18至10号规格的碳钢（M-1/P-1）至奥氏体不锈钢（M-8/P-8）的钨极气体保护焊标准焊接工艺规范（SWPS）带或不带衬垫

1A1W1S1 Archive Product 373

Standard WPS for Gas Tungsten Arc Welding with Consumable Inserts of Carbon Steel (M-1/P-1/S-1, Group 1 or 2), 1/8 through 1 1/2" Thick, INMs-1 and ER70S-2, As-Welded or PWHT Condition, Primarily Pipe Applications
1/8至1/2“厚、INMs-1和ER70S-2的碳钢（M-1/P-1/S-1 第1组或第2组）自耗插入件的气体保护钨极电弧焊标准焊接工艺规程焊态或焊后热处理条件下主要用于管道应用

1A1W1S1 Archive Product 535

Standard WPS for Gas Tungsten Followed by Shielded Metal Arc Welding of Carbon Steel (M-1/P-1/S-1, Group 1 or 2), 1/8 through 1 1/2" Thick, ER70S-2 and E7018, As-Welded or PWHT Condition, Primarily Pipe Applications
1/8至1/2“厚、ER70S-2和E7018的碳钢（M-1/P-1/S-1 第1组或第2组）在焊接或焊后热处理条件下进行钨极气体保护焊的标准WPS 主要用于管道应用

1A1W1S1 Archive Product 138

Standard Welding Procedure Specification (Swps) for Gas Tungsten Arc Welding of Carbon Steel to Austenitic Stainless Steel (M-1, P-1 or S-1 to M-8, P-8, or S-8), 18 through 10 Gauge, in the As-Welded Condition, with or without Backing
碳钢与奥氏体不锈钢（M-1、P-1或S-1至M-8、P-8或S-8）在焊态条件下18至10 Gauge（带或不带衬垫）的钨极气体保护焊标准焊接工艺规范（Swps）

AWS B2.1-5A-224-1999(R2009)

Standard Welding Procedure Specification (SWPS) for Gas Tungsten Arc Welding followed by Shielded Metal Arc Welding of Chromium-Molybdenum Steel (M-5A/P-5A), 1/8 through 1/2 in. Thick, As-Welded Condition; 1/8 through 1-1/2 in. Thick, PWHT Condition, ER90S-B3 and E9018-B3, Primarily Pipe Applic
1/8至1/2英寸铬钼钢（M-5A/P-5A）的气体保护钨极电弧焊后的标准焊接工艺规范（SWPS）厚如焊接状态；1/8至1-1/2英寸厚度焊后热处理条件 ER90S-B3和E9018-B3 主要用于管道应用

《国家标准化发展纲要》提出建设国家数字标准馆，推动标准化工作向数字化、网络化、智能化转型。中国标准化研究院正在全力推进国家数字标准馆建设，力争在2026年底建成“一个中心”和“一个平台”，即全球领先的标准数据资源中心，涵盖标准全生命周期的数字化、网络化、智能化研究与服务平台。

专题数据库

标准管理系统

大数据分析系统

标准智能研制系统