本文件规定了通过筛分分析测定涂层粉末粒度分布的方法。根据ISO 8130-13，通过激光衍射测定最大粒径小于100µm的粒径分布。该方法特别用于确定超大材料或是否存在污染，并可通过检查单个筛子上的残留量作为质量控制程序（“go”/“no go”测试）。 以下粒度是涂层粉末的典型粒度，但粒度可能会因应用而有所不同: -薄膜技术:1µm至63µm；-静电涂层:10µm至200µm；-流化床法:100µm及以上。 注:筛孔尺寸小于32µm的筛子不实用，在使用过程中可能会失明。交叉引用:ISO 8130-14ISO 565ISO 3310-1ISO 15528ISO 3310-2ISO 8130-13购买本文件时提供的所有当前修订版均包含在购买本文件中。

This document specifies a method for the determination of the particle size distribution of coating powders by sieve analysis. Particle size distributions with a maximum of less than 100 µm is determined by laser diffraction, ISO 8130-13. This method is used especially for determining the oversize material or for the presence of contamination and can be used as a quality control procedure ("go"/"no go" test) by checking the amount retained on a single sieve. The following particle sizes are typical for coating powders, however the particle size can deviate depending on the application: — thin-film technology: 1 µm to 63 µm;— electrostatic coating: 10 µm to 200 µm;— fluidizing-bed method: 100 µm and above. NOTE Sieves with a mesh size smaller than 32 µm are not practical and are likely to become blind during use.Cross References:ISO 8130-14ISO 565ISO 3310-1ISO 15528ISO 3310-2ISO 8130-13All current amendments available at time of purchase are included with the purchase of this document.