1.1 本规范 2. 包括UNS N08120、UNS N08800、UNS N08801、UNS N08810、UNS N08811、UNS N08890和UNS N06811，其形式为冷加工和热加工退火无缝管。合金UNS N08800和UNS N06811通常用于1100以下的工作温度 华氏度（593 °C）。合金UNS N08120、UNS N08810、UNS N08811和UNS N08890通常用于高于1100的工作温度 华氏度（593 °C），其中需要抗蠕变和断裂，并对其进行退火，以形成受控晶粒尺寸，从而在此温度范围内获得最佳性能。 1.2 以英寸-磅为单位的数值应视为标准值。括号中给出的值是到国际单位制的数学转换，仅供参考，不被视为标准值。 1.3 以下安全隐患警告仅适用于试验方法部分第节 7. ，符合本规范。 本标准并非旨在解决与其使用相关的所有安全问题（如有）。本标准的用户有责任在使用前制定适当的安全、健康和环境实践，并确定监管限制的适用性。 1.4 本国际标准是根据世界贸易组织技术性贸易壁垒（TBT）委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认标准化原则制定的。

1.1 This specification 2 covers UNS N08120, UNS N08800, UNS N08801, UNS N08810, UNS N08811, UNS N08890, and UNS N06811 in the form of cold-worked and hot-finished annealed seamless pipe and tube. Alloys UNS N08800 and UNS N06811 are normally employed in service temperatures up to and including 1100 °F (593 °C). Alloys UNS N08120, UNS N08810, UNS N08811, and UNS N08890 are normally employed in service temperatures above 1100 °F (593 °C) where resistance to creep and rupture is required, and they are annealed to develop controlled grain size for optimum properties in this temperature range. 1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 The following safety hazards caveat pertains only to the test method portion, Section 7 , of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.