1.1 本试验方法包括测定暴露在高湿度大气中的矿物纤维绝缘材料吸收的水蒸气量。本试验方法仅适用于纤维基材和粘合剂。通过本试验方法获得的结果不能用于描述贴面产品，因为未使用本试验方法测试贴面。 1.2 材料的水蒸气吸附特性可能受到温度升高或化学暴露等条件的影响。 根据本试验方法获得的数值可能无法充分描述受这些条件影响的材料的水蒸气吸附特性。 1.3 以国际单位制或英寸-磅单位表示的数值应单独视为标准值。每个系统中规定的值可能不是精确的等效值；因此，每个系统应相互独立使用。将两个系统的值合并可能会导致不符合标准。 1.4 本标准并非旨在解决与其使用相关的所有安全问题（如有）。本标准的用户有责任在使用前制定适当的安全、健康和环境实践，并确定监管限制的适用性。 1.5 本国际标准是根据世界贸易组织技术性贸易壁垒（TBT）委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认标准化原则制定的。 ====意义和用途====== 5.1 吸水会导致重量增加，并导致绝缘性能的潜在退化。

1.1 This test method covers the determination of the amount of water vapor sorbed by mineral fiber insulation exposed to a high-humidity atmosphere. This test method is applicable only to fibrous base material and binder. The results obtained by this test method cannot be used in describing faced products, since the facing is not tested by using this test method. 1.2 The water vapor sorption characteristics of materials may be affected by conditions such as elevated temperatures or chemical exposures. Values obtained as a result of this test method may not adequately describe the water vapor sorption characteristics of materials subjected to these conditions. 1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. ====== Significance And Use ====== 5.1 The sorption of water can result in an increase in weight and a resultant potential degradation of the properties of the insulation.