SAE AMS4179E-固溶热处理、应力消除和沉淀热处理的5.6Zn-2.5Mg-1.6Cu-0.23Cr（7175-T7452）铝合金锻件-国家数字标准馆

现行 SAE AMS4179E

到馆提醒

收藏跟踪

购买正版

Aluminum Alloy Forgings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7175-T7452) Solution Heat Treated, Stress Relieved, and Precipitation Heat Treated 固溶热处理、应力消除和沉淀热处理的5.6Zn-2.5Mg-1.6Cu-0.23Cr（7175-T7452）铝合金锻件

发布日期： 2023-09-28

本规范涵盖热处理时标称厚度不超过3英寸（76 mm）的模锻件和6英寸（150 mm）以下的手工锻件形式的铝合金，以及任何尺寸的锻件坯料（见8.7）。

This specification covers an aluminum alloy in the form of die forgings not over 3 inches (76 mm) and hand forgings up to 6 inches (150 mm), inclusive, in nominal thickness at the time of heat treatment, and forging stock of any size (see8.7).

分类信息

发布单位或类别：美国-美国机动车工程师协会

关联关系

研制信息

相似标准/计划/法规

Aluminum Alloy, Die and Hand Forgings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7175-T74) Solution and Precipitation Heat Treated
经固溶和沉淀热处理的5.6Zn-2.5Mg-1.6Cu-0.23Cr（7175-T74）铝合金模锻件和手锻件

Aluminum Alloy, Die Forgings, 5.6zn 2.5mg 1.6cu 0.23cr Solution and Precipitation Heat Treated
铝合金模锻 5.6zn 2.5mg 1.6cu 0.23cr固溶和沉淀热处理

Aluminum Alloy, Hand Forgings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T7452) Solution Heat Treated, Stress Relieved, and Precipitation Heat Treated
铝合金手工锻件5.6Zn-2.5Mg-1.6Cu-0.23Cr（7075-T7452）固溶热处理、应力消除和沉淀热处理

Aluminum Alloy, Die and Hand Forgings 5.6zn 2.5mg 1.6cu 0.23cr Solution Heat Treated and Aged
铝合金、模具和手工锻件5.6zn 2.5mg 1.6cu 0.23cr固溶热处理和时效

Aluminum Alloy, Extrusions 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7175-T73511) Solution Heat Treated, Stress Relieved by Stretching, Straightened, and Overaged
铝合金挤压件5.6Zn-2.5Mg-1.6Cu-0.23Cr（7175-T73511）固溶热处理通过拉伸、矫直和过度时效消除应力

Aluminum Alloy Die Forgings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T73) Solution and Precipitation Heat Treated
固溶和沉淀热处理的铝合金模锻件5.6Zn-2.5Mg-1.6Cu-0.23Cr（7075-T73）

Aluminum Alloy, Die and Hand Forgings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T74) Solution Heat Treated and Aged
铝合金、模具和手工锻件5.6Zn-2.5Mg-1.6Cu-0.23Cr（7075-T74）固溶热处理和时效

Aluminum Alloy, Hand Forgings, 5.6zn 2.5mg 1.6cu 0.23cr, Solution Heat Treated, Stress Relieved, and Precipitation Heat Treated
铝合金、手工锻件、5.6zn 2.5mg 1.6cu 0.23cr、固溶热处理、应力消除和沉淀热处理

Aluminum Alloy Forgings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T7352) Solution Heat Treated, Stress Relieved by Compression, and Overaged
铝合金锻件5.6Zn-2.5Mg-1.6Cu-0.23Cr（7075-T7352）固溶热处理通过压缩消除应力并过时效

Aluminum Alloy, Die and Hand Forgings and Rolled Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T6) Solution and Precipitation Heat Treated
经固溶和沉淀热处理的5.6Zn-2.5Mg-1.6Cu-0.23Cr（7075-T6）铝合金、模具和手工锻件及轧制环

Aluminum Alloy, Rolled or Forged Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved, and Precipitation Heat Treated
铝合金、轧制或锻造环5.6Zn-2.5Mg-1.6Cu-0.23Cr（7075-T651、7075-T652）固溶热处理、机械应力消除和沉淀热处理

Aluminum Alloy, Rolled or Forged Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T7351, 7075-T7352) Solution Heat Treated, Mechanically Stress Relieved, and Precipitation Heat Treated
铝合金、轧制或锻造环5.6Zn-2.5Mg-1.6Cu-0.23Cr（7075-T7351、7075-T7352）固溶热处理、机械应力消除和沉淀热处理

《国家标准化发展纲要》提出建设国家数字标准馆，推动标准化工作向数字化、网络化、智能化转型。中国标准化研究院正在全力推进国家数字标准馆建设，力争在2026年底建成“一个中心”和“一个平台”，即全球领先的标准数据资源中心，涵盖标准全生命周期的数字化、网络化、智能化研究与服务平台。

专题数据库

标准管理系统

大数据分析系统

标准智能研制系统