AS/NZS 2205.4.1:2019-金属焊缝的破坏性试验方法方法4.1:断裂试验-国家数字标准馆

现行 AS/NZS 2205.4.1:2019

到馆提醒

收藏跟踪

购买正版

Methods for destructive testing of welds in metal, Method 4.1: Fracture test 金属焊缝的破坏性试验方法方法4.1:断裂试验

发布日期： 2019-03-27

本标准的目的是规定试样的尺寸和进行断裂试验的程序，以获得有关内部缺陷类型、尺寸和分布的信息，如孔隙、裂纹、未熔合、未穿透和断裂表面上的固体夹杂物。

The objective of this Standard is to specify the sizes of test specimen and the procedures for carrying out fracture tests in order to obtain information about types, sizes and distribution of internal imperfections such as porosities, cracks, lack of fusion, lack of penetration and solid inclusions on the fracture surface.

分类信息

发布单位或类别：澳大利亚-澳大利亚/新西兰标准

关联关系

研制信息

相似标准/计划/法规

AS 2205.7.1-2003

Methods for destructive testing of welds in metal, Method 7.1: Charpy V-notch impact fracture toughness test
金属焊缝的破坏性试验方法方法7.1:夏比V型缺口冲击断裂韧性试验

AS 2205.7.2-2003

Methods for destructive testing of welds in metal, Method 7.2: Dropweight fracture toughness test for nil-ductility transition temperature
金属焊缝的破坏性试验方法方法7.2:零塑性转变温度下的落锤断裂韧性试验

AS 2205.2.2-2003

Methods for destructive testing of welds in metal, Method 2.2: All-weld-metal tensile test
金属焊缝的破坏性试验方法方法2.2:全焊缝金属拉伸试验

AS 2205.7.3-2003

Methods for destructive testing of welds in metal, Method 7.3: Fracture mechanics toughness tests (KIc, critical CTOD and critical J values)
金属焊缝破坏性试验方法方法7.3:断裂力学韧性试验（KIc、临界CTOD和临界J值）

AS 2205.6.1-2003

Methods for destructive testing of welds in metal, Method 6.1: Weld joint hardness test
金属焊缝的破坏性试验方法方法6.1:焊缝硬度试验

AS/NZS 2205.5.1-2019

Methods for destructive testing of welds in metal, Method 5.1: Macroscopic and microscopic examination of welds
金属焊缝的破坏性试验方法方法5.1:焊缝的宏观和微观检验

BS EN ISO 15653-2018

Metallic materials. Method of test for the determination of quasistatic fracture toughness of welds
金属材料焊缝准静态断裂韧性测定的试验方法

GB/T 28896-2023

金属材料焊接接头准静态断裂韧度测定的试验方法
Metallic materials—Method of test for the determination of quasistatic fracture toughness of welds

Metallic materials — Method of test for the determination of quasistatic fracture toughness of welds
金属材料 - 测量焊缝的准静态断裂韧性的测试方法

AS 2205.9.1-2003

Methods for destructive testing of welds in metal, Method 9.1: Hot cracking test
金属焊缝的破坏性试验方法方法9.1:热裂纹试验

Method for destructive testing of welds in metal, Method 1: General requirements for tests
金属焊缝的破坏性试验方法方法1:试验的一般要求

AS 2205.3.5-2003

Methods for destructive testing of welds in metal, Method 3.5: Tongue bend test
金属焊缝的破坏性试验方法方法3.5:舌弯曲试验

AS 2205.10.1-2003

Methods for destructive testing of welds in metal, Method 10.1: Corrosion test for welded austenitic stainless steel
金属焊缝的破坏性试验方法方法10.1:焊接奥氏体不锈钢的腐蚀试验

AS/NZS 2205.3.1-2020

Destructive tests on welds in metallic materials, Method 3.1: Bend tests
金属材料焊缝的破坏性试验方法3.1:弯曲试验

AS 2205.3.3-2003

Methods for destructive testing of welds in metal, Method 3.3: Longitudinal guided bend test
金属焊缝的破坏性试验方法方法3.3:纵向导向弯曲试验

AS 2205.3.2-2003

Methods for destructive testing of welds in metal, Method 3.2: Transverse free bend test
金属焊缝的破坏性试验方法方法3.2:横向自由弯曲试验

AS 2205.8.1-2003

Methods for destructive testing of welds in metal, Method 8.1: Longitudinal fillet shear test
金属焊缝的破坏性试验方法方法8.1:纵向角剪切试验

AS 2205.2.1-2003

Methods for destructive testing of welds in metal, Method 2.1: Transverse butt tensile test
金属焊缝的破坏性试验方法方法2.1:横向对接拉伸试验

AS 2205.8.2-2003

Methods for destructive testing of welds in metal, Method 8.2: Transverse fillet shear test
金属焊缝的破坏性试验方法方法8.2:横向圆角剪切试验

AS 2205.2.3-2003

Methods for destructive testing of welds in metal, Method 2.3: Transverse joggle-butt tensile test
金属焊缝的破坏性试验方法方法2.3:横向啮合对接拉伸试验

《国家标准化发展纲要》提出建设国家数字标准馆，推动标准化工作向数字化、网络化、智能化转型。中国标准化研究院正在全力推进国家数字标准馆建设，力争在2026年底建成“一个中心”和“一个平台”，即全球领先的标准数据资源中心，涵盖标准全生命周期的数字化、网络化、智能化研究与服务平台。

专题数据库

标准管理系统

大数据分析系统

标准智能研制系统