1.1 本试验方法包括通过使用J形环和模具来测定自密实混凝土（SCC）的通过能力。 1.2 以国际单位制或英寸-磅单位表示的数值应单独视为标准值。每个系统中规定的值可能不是精确的等效值；因此，每个系统应相互独立使用。将两个系统的值合并可能会导致不符合标准。 1.3 本标准的文本引用了提供解释材料的注释和脚注。这些注释和脚注（不包括表和图中的注释和脚注）不应视为本标准的要求。 1.4 本标准并非旨在解决与其使用相关的所有安全问题（如有）。本标准的用户有责任在使用前制定适当的安全和健康实践，并确定监管限制的适用性。 ( 警告- 新鲜的水硬性胶结混合物具有腐蚀性，长时间接触可能会导致皮肤和组织化学烧伤。 2. ) 1.5 本国际标准是根据世界贸易组织技术性贸易壁垒（TBT）委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认标准化原则制定的。 ====意义和用途====== 5.1 本试验方法提供了确定自密实混凝土通过能力的程序。本试验方法适用于实验室比较不同混凝土混合物的通过能力。它也适用于现场作为质量控制测试。 5.2 坍落度流和J形环流之间的差异表明混凝土的通过能力。 差值小于25毫米[1英寸]表示良好的通过能力和大于50毫米[2英寸]的差异表示传球能力差。J型环试验和不带J型环的坍落度流动试验的模具方向应相同。 5.3 本试验方法仅限于骨料标称最大尺寸不超过25 mm[1 in]的自固结混凝土。

1.1 This test method covers determination of the passing ability of self-consolidating concrete (SCC) by using the J-Ring in combination with a mold. 1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.3 The text of this standard references notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. ( Warning— Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure. 2 ) 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. ====== Significance And Use ====== 5.1 This test method provides a procedure to determine the passing ability of self-consolidating concrete. This test method is applicable for laboratory use in comparing the passing ability of different concrete mixtures. It is also applicable in the field as a quality control test. 5.2 The difference between the slump flow and J-Ring flow is an indication of the passing ability of the concrete. A difference less than 25 mm [1 in.] indicates good passing ability and a difference greater than 50 mm [2 in.] indicates poor passing ability. The orientation of the mold for the J-Ring test and for the slump flow test without the J-Ring shall be the same. 5.3 This test method is limited to self-consolidating concrete with nominal maximum size of aggregate of up to 25 mm [1 in.].