BS EN 10346:2015规定了低碳材料连续热浸镀锌产品的要求 冷成型用钢、建筑用钢和冷成型用高强度钢 含锌（Z）、锌铁合金（ZF）、锌铝合金（ZA）、铝锌合金（AZ）、铝硅合金 （AS）或锌镁合金（ZM），以及由多相钢制成的连续热浸镀锌产品 冷成型涂有锌（Z）、锌铁合金（ZF）、锌铝合金（ZA）或锌镁合金（ZM） 厚度为0.20毫米≤ t<3.0mm。根据询价和订购时的协议，本欧洲标准适用于连续热浸 厚度t<0.20mm或厚度 3.0毫米≤ T≤ 6.5mm，具有商定的机械性能和试样、涂层附着力和表面条件要求。厚度是涂层后交付产品的最终厚度。本文件适用于所有宽度的带材和从带材上切下的板材(≥ 600毫米（宽度）和切割长度 （<600毫米宽）。注1:也可提供涂有（纯）铝的产品，但不在本欧洲标准范围内。注2:本欧洲标准涵盖的产品用于冷成型性、高强度、规定的最小屈服强度和/或耐腐蚀性是最重要因素的情况。 产品的耐腐蚀性与涂层厚度成正比，因此与其质量成正比（另见7.3.2）。本欧洲标准涵盖的产品可用作EN 10169中规定的建筑和一般工程应用的有机涂层平板产品的基材。注3:根据询价和订购时的协议，本欧洲标准适用于其他连续热浸涂层热轧扁钢产品（例如，根据EN 10149-2）。交叉引用:EN 606EN 10020:2000EN 10021:2006EN 10027-1EN 10027-2EN 10049EN 10079:2007EN 10143EN 10204:2004EN 10325EN ISO 6892-1:2009ISO 10113ISO 10275EN 10149-2EN 10152EN 10169EN ISO 14713-1ISO 14713- 1:2009EN ISO 14713-2ISO 14713-2:2009购买本文件时可获得的所有现行修订均包含在购买本文件中。

BS EN 10346:2015 specifies requirements for continuously hot-dip coated products made of low carbon steels for cold forming, of steels for construction and of steels with high proof strength for cold forming coated with zinc (Z), zinc-iron alloy (ZF), zinc-aluminium alloy (ZA), aluminium-zinc alloy (AZ), aluminium-silicon alloy (AS) or zinc-magnesium alloy (ZM) and for continuously hot-dip coated products made of multiphase steels for cold forming coated with zinc (Z), zinc-iron alloy (ZF), zinc-aluminium alloy (ZA) or zinc-magnesium alloy (ZM) in thicknesses of 0,20 mm ≤ t < 3,0 mm.By agreement at the time of enquiry and order, this European Standard is applicable to continuously hot-dip coated flat products of an expanded validity range defined for thicknesses t < 0,20mm or in thicknesses 3,0 mm ≤ t ≤ 6,5 mm with agreed mechanical properties and test specimens, adhesion of coating and surface condition requirements.The thickness is the final thickness of the delivered product after coating.This document applies to strip of all widths and to sheets cut from it (≥ 600 mm width) and cut lengths (< 600 mm width).NOTE 1 Products coated with (pure) aluminium can also be available, but are not covered by this European standard.NOTE 2 The products covered by this European Standard are used where cold formability, high strength, a defined minimum yield strength and/or corrosion resistance are the most important factors. Corrosion resistance of the product is proportional to the coating thickness, hence to its mass (see also 7.3.2). The products covered by this European Standard can be used as substrates for organic coated flat products specified in EN 10169 for building and general engineering applications.NOTE 3 By agreement at the time of enquiry and order, this European Standard is applicable to other continuously hotdip coated hot rolled steel flat products (e.g. in accordance with EN 10149-2).Cross References:EN 606EN 10020:2000EN 10021:2006EN 10027-1EN 10027-2EN 10049EN 10079:2007EN 10143EN 10204:2004EN 10325EN ISO 6892-1:2009ISO 6892-1:2009ISO 10113ISO 10275EN 10149-2EN 10152EN 10169EN ISO 14713-1ISO 14713-1:2009EN ISO 14713-2ISO 14713-2:2009All current amendments available at time of purchase are included with the purchase of this document.