Aluminum Alloy, Extrusions 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T74511) Solution Heat Treated, Stress Relieved, Straightened, and Overaged 挤压铝合金6.2Zn-2.3Cu-2.2Mg-0.12Zr(7050-T74511)固溶热处理、消除应力、矫直和过度时效
发布日期: 2023-09-05
本规范涵盖标称直径或厚度为5.000英寸(127.00 mm)及以下、横截面积为32平方英寸(206 cm2)及以下的挤压棒材、棒材、线材、型材形式的铝合金,以及壁厚为3.000英寸(76.20 mm)及以上、横截面积为20平方英寸(129 cm2)及以上的管材(见8.5)。
This specification covers an aluminum alloy in the form of extruded bars, rods, wire, profiles 5.000 inches (127.00 mm) and under in nominal diameter or thickness and 32 square inches (206 cm2) and under in cross-sectional area, and tubing 3.000 inches (76.20 mm) and under in wall thickness and 20 square inches (129 cm2) and under in cross-sectional area (see8.5).
分类信息
关联关系
研制信息
相似标准/计划/法规
现行
SAE AMS4340G
Aluminum Alloy, Extrusions 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T76511) Solution Heat Treated, Stress Relieved, Straightened, and Overaged
铝合金 挤压件6.2Zn-2.3Cu-2.2Mg-0.12Zr(7050-T76511)固溶热处理、应力消除、矫直和过度时效
2018-04-10
现行
SAE AMS4341H
Aluminum Alloy, Extrusions, 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T73511), Solution Heat Treated, Stress Relieved by Stretching, Straightened, and Overaged
挤压铝合金 6.2Zn-2.3Cu-2.2Mg-0.12Zr(7050-T73511) 固溶热处理 拉伸、矫直和过时效消除应力
2024-01-16
现行
SAE AMS4050K
Aluminum Alloy, Plate 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7451) Solution Heat Treated, Stress Relieved, and Overaged
铝合金 板6.2Zn-2.3Cu-2.2Mg-0.12Zr(7050-T7451) 固溶热处理 应力消除和过时效
2021-04-22
现行
SAE AMS4201G
Aluminum Alloy Plate 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7651) Solution Heat Treated, Stress Relieved, and Overaged
铝合金板6.2Zn-2.3Cu-2.2Mg-0.12Zr(7050-T7651)固溶热处理、应力消除和过度时效
2020-08-20
现行
SAE AMS4243C
Aluminum Alloy, Alclad Sheet 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (Alclad 7050-T76) Solution Heat Treated and Overaged
铝合金 包铝板6.2Zn-2.3Cu-2.2Mg-0.12Zr(包铝7050-T76)固溶热处理和过时效
2020-01-13
现行
SAE AMS4333E
Aluminum Alloy, Die Forgings 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) Solution Heat Treated, Compression Stress-Relieved, and Overaged
铝合金 模锻件6.2Zn-2.3Cu-2.2Mg-0.12Zr(7050-T7452)固溶热处理 消除压缩应力 并过时效
2022-06-09
现行
SAE AMS4108F
Aluminum Alloy, Hand Forgings 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) Solution Heat Treated, Compression Stress-Relieved, and Overaged
铝合金 手工锻件6.2Zn-2.3Cu-2.2Mg-0.12Zr(7050-T7452)固溶热处理 消除压缩应力 并过时效
2015-10-28