Aluminum Alloy Plate 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7651) Solution Heat Treated, Stress Relieved, and Overaged 铝合金板6.2Zn-2.3Cu-2.2Mg-0.12Zr（7050-T7651）固溶热处理、应力消除和过度时效

发布日期： 2020-08-20

本规范涵盖标称厚度为0.250至3.000英寸（6.35至76.20毫米）的板状铝合金（见8.5）。

This specification covers an aluminum alloy in the form of plate 0.250 to 3.000 inches (6.35 to 76.20 mm) in nominal thickness (see8.5).

分类信息

发布单位或类别：美国-美国机动车工程师协会

关联关系

研制信息

相似标准/计划/法规

现行

SAE AMS4050K

Aluminum Alloy, Plate 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7451) Solution Heat Treated, Stress Relieved, and Overaged
铝合金板6.2Zn-2.3Cu-2.2Mg-0.12Zr（7050-T7451）固溶热处理应力消除和过时效

2021-04-22

现行

SAE AMS4243C

Aluminum Alloy, Alclad Sheet 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (Alclad 7050-T76) Solution Heat Treated and Overaged
铝合金包铝板6.2Zn-2.3Cu-2.2Mg-0.12Zr（包铝7050-T76）固溶热处理和过时效

2020-01-13

现行

SAE AMS4340G

Aluminum Alloy, Extrusions 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T76511) Solution Heat Treated, Stress Relieved, Straightened, and Overaged
铝合金挤压件6.2Zn-2.3Cu-2.2Mg-0.12Zr（7050-T76511）固溶热处理、应力消除、矫直和过度时效

2018-04-10

现行

SAE AMS4342G

Aluminum Alloy, Extrusions 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T74511) Solution Heat Treated, Stress Relieved, Straightened, and Overaged
挤压铝合金6.2Zn-2.3Cu-2.2Mg-0.12Zr（7050-T74511）固溶热处理、消除应力、矫直和过度时效

2023-09-05

现行

SAE AMS4333E

Aluminum Alloy, Die Forgings 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) Solution Heat Treated, Compression Stress-Relieved, and Overaged
铝合金模锻件6.2Zn-2.3Cu-2.2Mg-0.12Zr（7050-T7452）固溶热处理消除压缩应力并过时效

2022-06-09

现行

SAE AMS4341H

Aluminum Alloy, Extrusions, 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T73511), Solution Heat Treated, Stress Relieved by Stretching, Straightened, and Overaged
挤压铝合金 6.2Zn-2.3Cu-2.2Mg-0.12Zr（7050-T73511）固溶热处理拉伸、矫直和过时效消除应力

2024-01-16

现行

SAE AMS4108F

Aluminum Alloy, Hand Forgings 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) Solution Heat Treated, Compression Stress-Relieved, and Overaged
铝合金手工锻件6.2Zn-2.3Cu-2.2Mg-0.12Zr（7050-T7452）固溶热处理消除压缩应力并过时效

2015-10-28