1.1 本试验方法包括在规定的制备和试验条件下，以约90度的角度进行试验时，测定一个刚性被粘物和一个柔性被粘物之间粘合剂的抗剥离强度。 1.2 粘附物厚度的变化通常会影响测试值。因此，材料规范中应规定用于制作试样的粘附物的厚度。当未规定厚度时，柔性被粘物应为0.60 mm（0.025 in.）厚度和刚性粘附物应为1.60 mm（0.060 in.）厚的 注1: 一种较重的织物，如帆布，已被用作灵活的粘附物。 1.3 以国际单位制表示的数值应视为标准。括号中给出的值仅供参考。 1.4 本标准并非旨在解决与其使用相关的所有安全问题（如有）。 本标准的用户有责任在使用前制定适当的安全、健康和环境实践，并确定监管限制的适用性。 1.5 本国际标准是根据世界贸易组织技术性贸易壁垒（TBT）委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认标准化原则制定的。 ====意义和用途====== 5.1 该测试方法适用于验收和质量控制测试。被粘物、应用程序和样品处理应经被粘物和粘合剂的制造商和用户同意。

1.1 This test method covers the determination of the resistance-to-peel strength of an adhesive bond between one rigid adherend and one flexible adherend when tested at an angle of approximately 90 degrees under specified conditions of preparation and testing. 1.2 A variation in thickness of the adherends will generally influence test values. For this reason, the thickness of the adherends used to make the test specimens shall be specified in the material specification. When no thickness is specified, the flexible adherend shall be 0.60 mm (0.025 in.) thick and the rigid adherend shall be 1.60 mm (0.060 in.) thick. Note 1: A heavy fabric, such as canvas, has been used as a flexible adherend. 1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. ====== Significance And Use ====== 5.1 This test method is useful for acceptance and quality control testing. Adherends, application procedure, and sample conditioning shall be as agreed upon by the manufacturer and the user of the adherends and the adhesive.