1.1 本试验方法旨在作为一种测量复合木基材涂层或未涂层边缘膨胀和开裂的方法，该复合木基材已被含有表面活性剂的试验溶液润湿。 1.2 以国际单位制表示的数值应视为标准。括号中给出的值仅供参考。 1.3 本标准并不旨在解决与其使用相关的所有安全问题（如有）。本标准的使用者有责任在使用前制定适当的安全、健康和环境实践，并确定监管限制的适用性。 1.4 本国际标准是根据世界贸易组织技术性贸易壁垒委员会发布的《关于制定国际标准、指南和建议的原则的决定》中确立的国际公认的标准化原则制定的。 ====意义和用途====== 5.1 该测试方法提供了在加速的水分应力下各种复合木制品的涂层边缘的尺寸稳定性和完整性的测量。它被广泛用作复合木制品在外部暴露期间预期性能的指标或预测指标。它可用于涂层、基材或两者的开发评估。它还可用于有涂层或无涂层的复合木制品的生产的质量控制或监测。

1.1 This test method is intended to serve as a means for measurement of swelling and cracking of the coated or uncoated edge of a composite wood substrate that has been subjected to wetting by a test solution containing surface active agent. 1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. ====== Significance And Use ====== 5.1 This test method provides a measure of the dimensional stability and integrity of the coated edge of various composite wood products under accelerated moisture stress. It is widely used as an indicator or predictor of the anticipated performance of composite wood products during exterior exposure. It may be used for developmental evaluation of coatings, substrates, or both. It may also be useful for quality control or monitoring of the production of coated or uncoated composite wood products.