IEC 60317-28:2013+AMD1:2024 CSV规定了180级漆包矩形铜绕组线的要求，其底涂层基于聚酯酰亚胺树脂，只要保留原始树脂的化学特性并满足所有规定的电线要求，可以对其进行改性。注-改性树脂是经过化学变化的树脂，或含有一种或多种添加剂以增强某些性能或应用特性的树脂。本标准涵盖的标称导体尺寸范围为: -宽度:最小。2.0 mm最大16.0 mm； -厚度:最小。最大0.80毫米。5.60毫米。本规范包括1级和2级导线，适用于所有导线。宽度和厚度的规定组合以及规定的宽度/厚度比在IEC 60317-0-2:2013.这第二版取消并取代了1990年出版的第一版，修正案1:19 97和修正案2:20 07。本版构成技术修订版。与上一版相比，此版本包括以下重大技术变更: -载有关于绕组线的一般说明的新子条款，以前是范围的一部分； -修订IEC 60317-0-2:20 13的参考文献，以阐明其应用是规范性的； -新3.3，外观； -删除第22条，高温失效； -对第23条的修改，针孔测试。关键词:漆包矩形铜绕组线要求，180级，聚酯酰亚胺树脂基底涂层 本出版物应与IEC 60317-0-2:20 13一起阅读。

IEC 60317-28:2013+AMD1:2024 CSV specifies the requirements of enamelled rectangular copper winding wire of class 180 with a sole coating based on polyesterimide resin, which may be modified providing it retains the chemical identity of the original resin and meets all specified wire requirements. NOTE - A modified resin is a resin that has undergone a chemical change, or contains one or more additives to enhance certain performance or application characteristics. The range of nominal conductor dimensions covered by this standard is:
- width: min. 2,0 mm max. 16,0 mm;
- thickness: min. 0,80 mm max. 5,60 mm. Wires of grade 1 and grade 2 are included in this specification and apply to the complete range of conductors. The specified combinations of width and thickness as well as the specified width/thickness ratio are given in IEC 60317-0-2:2013. This second edition cancels and replaces the first edition published in 1990, Amendment 1:1997 and Amendment 2:2007. This edition constitutes a technical revision. This edition includes the following significant technical changes with respect to the previous edition:
- new subclause containing general notes on winding wire, formerly a part of the scope;
- revision to references to IEC 60317-0-2:2013 to clarify that their application is normative;
- new 3.3, Appearance;
- deletion of Clause 22, High temperature failure;
- modification to Clause 23, Pin hole test. Keywords: requirements of enamelled rectangular copper winding wire, class 180, sole coating based on polyesterimide resin

This publication is to be read in conjunction with IEC 60317-0-2:2013.